Direct Fabrication of Cobalt Oxide Nano-particles Employing Glycine as a Combustion Fuel

Combustion method has been used as a fast and facile method to prepare nanocrystalline Co3O4 spinel employing glycine as a combustion fuel. The products were characterized by thermal analyses (TGA & DTA), X-ray diffraction technique (XRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM), and Transmission electron microscopy (TEM) techniques. Experimental results revealed that the molar ratio of fuel/oxidant play an important role in controlling the crystallite size of Co3O4 nanoparticles. Transmission electron microscopy indicated that the crystallite size of Co3O4 nanocrystals were in the range of 14–31 nm. Since the particle size of the powdered samples were found to be equivalent from both TEM and X-ray diffraction technique. X-ray diffraction confirmed the formation of CoO phase with spinel Co3O4. The effect of calcination temperature on crystallite size and morphology has been discussed.


Introduction
Transition metal oxides have attracted the attention of scientific researchers due to their promising applications in various fields. Among of these metal oxides cobalt oxide Co 3 O 4 , one of the most active catalyst for the total oxidation of methane 1 . Cobalt oxide has a wide range of applications in N 2 O decomposition, oxidation of volatile organic compounds (VOCs), Fischer-Tropsch synthesis (FTS), steam reforming of ethanol, low temperature CO oxidation, and hydrogen peroxide decomposition [2][3][4][5][6][7] . It is well known that the properties of Co 3 O 4 catalyst are strongly depending on its shape and size. Co 3 O 4 with nanosized have high surface area is expected to lead to even more attractive applications in conjunction of their traditional arena and nanotechnology 8 . Therefore, it is important to prepare Co 3 O 4 with defined morphologies and a narrow range of size distribution. Much effort has been made to synthesize Co 3 O 4 catalyst from economical and practical aspects point of view including micro-emulsion, thermal decomposition of cobalt oxalate, one-pot hydrothermal reaction, and sol-gel [9][10][11][12] . In addition, there are some reports involving the synthesis of Co 3 O 4 nanocrystallites with various morphologies. For instance, Co 3 O 4 crystallites with different morphologies such as urchin, spherical and quasi-cubic morphology were obtained by soft chemical method 13 . Co 3 O 4 nanocubes were prepared by hydrothermal oxidation method 14 . Co 3 O 4 nanorods were synthesized by molten salt approach 15 . Sphere-like Co 3 O 4 nanocrystals was synthesized by simple polyol route 16 , and combustion method using urea as a fuel 17 .
In recent years, combustion synthesis (CS) or self-propagating high-temperature synthesis (SHS) has been used as a facile technique for preparation of catalysts, alloys, composites and nanomaterials. CS is classified into two groups, depending upon the nature of reactants: (i) solid state combustion (SSC), and (ii) solution combustion synthesis (SCS). In SSC, initial reactants, intermediates and final products are all in the solid state. The disadvantages of this method are that the heterogeneity for the initial solid reactants is on the order of 10-100 μm. This feature, coupled with high reaction temperatures (>2000 K), makes it difficult to synthesize nanosize structures with high surface area 18 . SCS has emerged as an effective, fast, simple and low cost method for synthesize of a variety of nanosize materials. This process involves self-sustained reaction in homogeneous solutions of metal nitrates (oxidizer) and fuels (i.e., glycine, citric acid, urea … etc.). It yield homogenous, crystalline, and high-purity product. Glycine has been used as a fuel to synthesize different nanomaterials [19][20][21] . Grover et al. have prepared nanocrystalline ceria-doped-zirconia powder using glycine as a fuel 19  In the present work, we report a facile, convenient, fast, and inexpensive method to prepare Co 3 O 4 nanoparticles via SCS using glycine as a combustion fuel and cobalt nitrate as oxidizer. Our investigation studies the effect of fuel to oxidant molar ratios (F/O) as well as the calcination temperature in controlling particle size and morphology of prepared Co 3 O 4 . The textural and structure properties of the prepared Co 3 O 4 nano-particles were characterized by means of thermal analyses (TGA & DTA), X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and electron microscopy (SEM & TEM).

Preparation Procedure
Cobalt nitrate, Co(NO 3 ) 2 . 6H 2 O, and glycine, (NH 2 CH 2 COOH), were of analytical grade reagents and were used without further purification. Distilled water was used in all of preparations. A schematic representation of the synthesis procedure used in the synthesis of nano-crystalline Co 3 O 4 is schematically shown in Fig. 1. Two series of samples were prepared. In the first one (series I) we have investigated the effect of changing the glycine/cobalt molar ratios (F/O), 0.5, 1, 1.5, 2, 5, 8 and 16 on the morphology and crystallite size of Co 3 O 4 . In a typical procedure, the required amounts of cobalt nitrate and glycine were weighed to the nearest milligram. Cobalt nitrate and glycine were dissolved in 100 ml of distilled water to form a pink homogeneous solution; the solution was then heated on a hotplate at about 100℃ to evaporate the excess water. After that the obtained viscous gel were calcined in muffle furnace at 400℃ for 3h in a static air atmosphere. In series II, we have investigated the effect of changing the calcinations temperature, 350-1000 ℃ employing the same procedure and a glycine/cobalt molar ratio of 0.5.

Characterization
Simultaneous TGA and DTA curves were recorded with a shimadzu DTG-60 instrument apparatus using a heating rate of 10 ℃ min -1 in air atmosphere (flow rate 40 ml/min). Powder X-ray diffraction (XRD) patterns were recorded using Philips diffractometer (type PW 103/00) with CuKα radiation (λ = 1.5405 Ǻ) at 35 kV and 20 mA with a scanning rate in 2θ of 0.06 min -1 . FTIR spectra were performed employing the KBr disc technique in the wavelength range 4000-400cm -1 , using Thermo-Nicolet-6700 FTIR spectrophotometer. Scanning electron micrographs were obtained using a JEOL scanning microscope (model JSM-5400 LV). Transmission electron pictures were taken using JEOL transmission microscope (model JEMTH-100 II).

Thermal Analysis
Fig.2 shows the weight loss (TG) and the associated derivative thermogram (DTG) of the precursor synthesized at F/O equal 0.5 in air atmosphere as a carrier gas. This figure manifests that the precursor underwent four-step decomposition with increasing the temperature from ambient till 915℃. The first step starts from room temperature till around 145℃ which brings a weight loss (WL) of 27 %. This step can be ascribed to dehydration, deamination, starting of decarboxylation, and denitration of the precursor. The second step exhibits a weight loss of 27.4 %, within a narrow temperature range 145-190℃. It can be associated to simultaneous melting of the precursor and continuous denitration of remaining nitrates coming from cobalt precursor. The third step at 260℃ with a weight loss of 9 % could be attributed to the complete decomposition of the precursor and formation of spinel Co 3 O 4 . Further heating the precursor up to 1000℃, one can observe the fourth step at 915℃. This step is accompanied by weight loss of 2.5 % due to the decomposition of Co 3 O 4 into CoO [2] according to the following equation: Fig.2 shows a magnification of both the heating and the cooling curves of the precursor at the 800℃ till 1000℃ temperature range. It illustrates that the cooling of CoO phase formed at 915℃, as a product of the decomposition of spinel Co 3 O 4 phase, has a weight gain of 2.5 %. This weight gain could be attributed to the oxidation of CoO into Co 3 O 4 , and this in turn, indicates the reversibility of the above equation. It is worth to noting that, in case of lower fuel/oxidant molar ratio (i.e. 0.5) a multi-step decomposition of precursor was observed. On increasing the F/O to a value of two the obtained thermogram (not shown) these multistep processes emerged only as a single WL step. Fig. 3 shows the obtained DTA curve during heating the precursor with F/O molar ratio of 0.5 in air atmosphere till 1000℃. Inspection of this figure reveals the presence of Glycine as a Combustion Fuel distinct two-endothermic peaks at the 25-92℃ temperature range. Such effects could be related to the dehydration of the precursor. In addition, the thermogram shows a sharp exothermic peak at 141℃. The temperature of such peak is consistent with that of the first WL step observed in the TGA pattern. This effect corresponds to simultaneous evolving of NO 3 − and glycine. Simultaneously, glycine is oxidized by nitrate anions (resulting carbon dioxide, nitrogen, nitrogen dioxide and water 22 ) releasing plenty of gases. Thus, the exothermic peak could be attributed to the combustion of evolved gases. The narrow endothermic peak at 194 ℃ associated with the second WL step in TGA. This endothermic peak related to melting of the precursor and simultaneously, continuous decomposition of cobalt nitrate hexahydrate. It is well known that, combustion consist of three components namely fuel, oxidizer and ignition temperature. Fuel is capable of burning by braking C-H bonds or gaining electrons from the oxidizer. Insufficient fuel will make the combustion process incomplete. Thus, the observed endothermic peak corresponds to the melting and continuous decomposition of the precursor. In this context, DTA of the precursor with F/O of 2 did not show this endothermic effect (as shown in Fig. 4). The observed exothermic peak at 263 ℃ corresponds to complete decomposition of the precursor and crystallization of Co 3 O 4 spinel. Going to the high temperature range the obtained DTA thermogram manifests the presence of an endothermic peak at 915 ℃ . Such effect can be ascribed to the decomposition of Co 3 O 4 into CoO 2 , i.e. thermal reduction of Co 3+ to Co 2+ .   20 have prepared nanosized CoFe 2 O 4 phase with a minor amount of CoO, when using glycine alone as a fuel. Thus, combustion synthesis using glycine is proposed to be a route to synthesis reduced oxidation state compounds such as CoO phase 20 .
In order to check the role of glycine molar ratio in changing the structural parameters of Co 3 O 4 such as lattice parameter (a) andcrystallite size (D). The lattice parameters were computed using the d-spacing values and the respective (hkl) parameters. The obtained results are plotted in Fig. 6-a. The crystallite size (D) was calculated using scherrer equation 21 Fig. 6-a shows the effect of the molar ratio variation on the lattice parameter of Co 3 O 4 . It is obvious that the variation of the lattice parameter with molar ratio follows the same trend as that observed for the crystallite size, i.e. lower molar ratio value leads to lower lattice parameter. Accordingly, one can state safely that the obtained nano-scaled Co 3 O 4 samples by SCS are attributed to two factors: (i) first, the reactants are mixed in the liquid state, which allows the uniform distribution of the reactants at atomic or molecular levels. (ii) Second, the high temperature of combustion reaction and short reaction time, which enable the formation and evolution of various gases that inhibit the growth of particle size and formation of nano-sized Co 3 O 4 .
Since the Co 3 O 4 obtained by using a molar ratio of 0.5 exhibits the lowest crystallite size, the study was extended to check the influence of changing the calcination temperature on the morphology and crystallite size of Co 3 O 4 at this ratio. XRD patterns of the as-prepared Co 3 O 4 obtained via calcining glycine/cobalt parents having molar ratio of 0.5 at 350-1000℃ temperature range are shown in Fig.7 a-h. From this figure two points could be raised: (i) all diffraction peaks belong to one phase only (Co 3 O 4 ), and (ii) No diffraction peaks related to CoO appear even at high temperatures (i.e. 900 or 1000℃) indicating that the final product of high purity. This is in a good agreement with the thermal analysis results (Fig. 2) by confirming the reversibility of equation 1, i.e. CoO when formed at high temperature it spontaneously converted to Co 3 O 4 on cooling. Table 2 gives the average crystallite size of Co 3 O 4 phase at different calcination temperatures (350-1000℃) calculated from XRD data, whereas the relevant lattice parameters are shown in Fig. 6-b. From these data one can state safely that, the sample calcined at 400℃ exhibits the lowest average crystallite size (D = 15.3 nm). With increasing the calcination temperature the average crystallite size is also increased. Accordingly, the optimum conditions to obtain pure Co 3 O 4 with smallest crystallite size using glycine as a fuel is glycine/cobalt ratio of 0.5 and a calcination temperature at 400℃.

Infrared Spectra
Cubic spinel structure of Co 3 O 4 with Co 2+ (3d 7 ) and Co 3+ (3d 6 ) located at tetrahedral and octahedral sites, respectively, belongs to the space group (Fd3m) 16 . The group theory predicts the following modes in the spinel 23 : Γ=A 1g (R)+E g (R)+F 1g (in)+3F 2g (R)+2A 2u (in)+2E u (in)+4F 1u (IR)+2F 2u (in), where (R), (IR) and (in) represent Raman active vibrations, infrared-active vibration and inactive modes, respectively. The FT-IR spectra of as-prepared nanocrystalline Co 3 O 4 at different F/O molar ratios being calcined at 400℃ are shown in Fig. 8 (curves a-g). In the investigated region (4000-400 cm -1 ), the entire obtained spectra manifest the presence of two absorption bands at 576 (υ 1 ) and 661(υ 2 ) cm -1 ; which originate from the stretching vibrations of the metal-oxygen bond and confirm the formation of Co 3 O 4 spinel oxide 2 . The υ 1 band is characteristic of OB 3 (where B denotes the Co 3+ in the octahedral hole) vibration and the υ 2 band is attributable to the ABO 3 (where A denotes the Co 2+ in the tetrahedral hole) vibration in the spinel lattice. In addition, the intensities of the peaks are decreased and become broader with increasing F/O value. Also, the FT-IR spectra show no residual organic compounds and NO 3 after calcinations. It is worth noting that, it is very difficult to differentiate between the FT-IR spectra of pure Co 3

Electron Microscopy (SEM&TEM)
The SEM micrographs of the synthesized Co 3 O 4 calcined at 400℃ for F/O ratios of 1 and 5 are shown in Fig. 9-a and -b, respectively. Inspection of this figure manifests that the prepared spinel Co 3 O 4 shows a porous network as a consequence of the gases escaping during the combustion process. Moreover, it is obvious that the nano-particles are uniform hollow tubular shapes with voids and holes randomly distributed among them. Particles of Co 3 O 4 are agglomerated regardless of the F/O molar ratio but the degree of agglomeration is increased with increasing F/O molar ratio. It is clear that, the lower F/O molar ratio gives lower particle sizes and this is in good agreement with the size determined by XRD analysis (Table 1). These features could be attributed to the expectedly higher exothermicity associated with higher F/O ratio.
The TEM micrographs of the synthesized Co 3 O 4 at F/O 0.5 being calcined at 400 and 1000 ℃ are shown in Fig.10-a and -b, respectively. The TEM micrographs show the nano-crystalline nature of the prepared Co 3 O 4 spinel. Fig.10-a, shows that the particles size in the range of 14-16 nm. These results are in a good agreement with the sizes determined from XRD analysis (Table 2). Moreover, the particles of this sample have homogeneous, weak agglomeration and uniform distribution in the powder sample. Inspection of Fig.10 (b) revealed that, thermal treatment of the precursor at elevated temperatures plays a significant role on the variation of particle size and morphology of Co 3 O 4 spinel. In this case, it could be seen that the particle size in the range of 28-31 nm, which is again in close agreement with the sizes determined from XRD analysis ( Table 2). Particles of Co 3 O 4 calcined at elevated temperatures are more agglomerated than that at lower one. As a conclusion, the F/O ratio has clearly important role on the structural and morphological properties of the powders. Low F/O ratios are recommended in this case in order to avoid agglomeration of the particles and to obtain powders with small particle size. Also, products with low calcinations temperatures are recommended for the same reason.

Conclusions
It is well known that combustion synthesis is an efficient, quick, simple, low cost and straightforward method for preparation of nanosized materials at lower temperatures. In this work we have prepared spinel Co 3 O 4 employing solution combustion synthesis (SCS) using glycine as a fuel. Glycine content is the key factor that controls the formation of reduced oxidation state compounds such as CoO phase. The ratio of the fuel to nitrates dramatically influenced the phase formation of the final products and the particle size. When the ratio of fuel to nitrates was (1.5-5) the final products were attributed to Co 3 O 4 and CoO phases, but at lower (0.5-1) or higher ratios (8-16) the final product were mainly spinel Co 3 O 4 phase. The morphology of the as-prepared Co 3 O 4 is a hollow nanotubular. The calcined powders showed the presence of regular particles, with narrow particle size distribution. In addition, this methodology can lead the system to a good chemical homogeneity as the reagents were mixed in an aqueous solution.